1060 Pure Aluminum Sheet Plate
Al metal alloy: 1060 grade
Alloy Group: 1XXX
Alu temper: O - H112 etc
Width: 100mm - 2600mm
Length: 100mm - 16000mm
Thickness: 0.2mm - 600mm
Technology: hot rolled ( DC ), cold rolling ( CC ), cast
Standard: ASTM B209, GB/T 3880, EN AW, DIN, MSRR, AMS, JIS, AISI, BS etc
Custom serivce: acceptable ( OEM, ODM etc )
Port of Loading: Qingdao, Shanghai, Guangzhou etc China main port
Certifications: GB/T19001-2016/ISO9001:2021, CE, SGS etc
What is 1060 Aluminum Sheet
The 1060 pure aluminum sheet belongs to the 1000 series aluminum sheet, which is quite similar to the 1050 aluminum alloy whose weight percentage of aluminum exceeds 0.1%.
Huawei AL's 1050 and 1060 aluminum sheets are both ISO compliant, but they cover different ASTM standards. 1060 aluminum alloy contains 0.05% copper, so its conductivity is 55%.
In addition, 1060 aluminum sheet has relatively low strength, basically pure aluminum alloy, with many different tempering states, such as O (annealed), H12, H14, H16, H18, etc. In addition, other aluminum plates belonging to the commercial pure wrought series are also available, including 1050, 1070, 1100, etc.
1060 Aluminum Sheet Feature
1060 aluminum sheet has good elongation and tensile strength, which can fully meet the high formability requirements of conventional processing (stamping, drawing).
For industrial pure aluminum, the plasticity, corrosion resistance, electrical conductivity and thermal conductivity are all high, but the strength is low, the heat treatment cannot be improved, and the workability is poor; gas welding, hydrogen welding and resistance welding are not easy to braze; under various pressures Machining and extending, bending.
The Heat Treatment Process Of 1060 Aluminum Sheet
Rapid annealing: the heating temperature is 350~410 degrees Celsius; under the effective thickness of the material, the holding time is 30-120 minutes; cooling in air or water.
High temperature annealing: The heating temperature is 350 ~ 500 ℃; if the thickness of the finished product is not less than 6mm, the holding time is 10 ~ 30 minutes, if the thickness is less than 6mm, heat until all the plates become hot and cool in the air.
Low temperature annealing: heating temperature is 150 ~ 250 ℃; holding time is 2 ~ 3H in air or water cooling.
1060 Aluminum Sheet Applications
1060 aluminum sheet is widely used in signs, billboards, building exterior wall decoration, bus body, high-rise building and factory wall decoration, kitchen sink, lamp holder, fan blade, electronic parts, chemical equipment, mechanical parts, sheet or spinning concave Deep drawing of shaped utensils, welded parts, heat exchangers, clock faces and plates, plates, kitchenware, decorations, reflective equipment, making automotive heat shields, chemical and marine equipment, etc.
1060 Aluminum Sheet Chemical Composition
| Elements | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others | Al | |||
| Content (max) | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | - | 0.05 | 0.03 | 0.15 | Remain | |||
| Alloy Temper | Specified | Tensile | Yield | Elongation(%) |
| Thickness(in.) | strength(ksi) | strength(ksi) | ||
| 1060-O(annealed) | 0.006-0.019 | 8.0-14.0 | 2.5 | Min15 |
| 0.020-0.050 | Min22 | |||
| 0.051-3.000 | Min25 | |||
| 1060-H12/1060-H22 | 0.017-0.050 | 11.0-16.0 | 9 | Min6 |
| 0.051-2.000 | Min12 | |||
| 1060-H14/1060-H24 | 0.006-0.019 | 12.0-17.0 | 10 | Min1 |
| 0.020-0.050 | Min5 | |||
| 0.051-1.000 | Min10 | |||
| 1060-H16/1060-H26 | 0.006-0.019 | 14.0-19.0 | 11 | Min1 |
| 0.020-0.050 | Min4 | |||
| 0.051-0.162 | Min5 | |||
| 1060-H18/1060-H28 | 0.006-0.019 | Min16.0 | Min12.0 | Min1 |
| 0.020-0.050 | Min3 | |||
| 0.051-0.128 | Min4 | |||
| 1060-H112 | 0.250-0.499 | Min11.0 | Min7.0 | Min10 |
| 0.500-1.000 | Min10.0 | Min5.0 | Min20 | |
| 1.001-3.000 | Min9.0 | Min4.0 | Min25 |